Sci Technol Adv Mater. 2018 Jul 16;19(1):495-506. doi: 10.1080/14686996.2018.1471653. eCollection 2018.

3D printed porous β-Ca₂SiO₄ scaffolds derived from preceramic resin and their physicochemical and biological properties.

Fu S¹, Liu W², Liu S¹, Zhao S², Zhu Y^1,3,4.

Abstract

Silicate bioceramic scaffolds are of great interest in bone tissue engineering, but the fabrication of silicate bioceramic scaffolds with complex geometries is still challenging. In this study, three-dimensional (3D) porous β-Ca₂SiO₄ scaffolds have been successfully fabricated from preceramic resin loaded with CaCO₃ active filler by 3D printing. The fabricated β-Ca₂SiO₄ scaffolds had uniform interconnected macropores (ca. 400 μm), high porosity (>78%), enhanced mechanical strength (ca. 5.2 MPa), and excellent apatite mineralization ability. Importantly, the results showed that the increase of sintering temperature significantly enhanced the compressive strength and the scaffolds sintered at higher sintering temperature stimulated the adhesion, proliferation, alkaline phosphatase activity, and osteogenic-related gene expression of rat bone mesenchymal stem cells. Therefore, the 3D printed β-Ca₂SiO₄ scaffolds derived from preceramic resin and CaCO₃ active fillers would be promising candidates for bone tissue engineering.